Category: Glaze
Created 2017-11-29 14:09:54 by Clemson University---Ceramic Dept.
Categories: Glaze
Firing Temperature: Δ05-04
Atmospheres: Oxidation
Surface Type: Glossy
Transparency: Transparent

Wood's Transparent Orange glaze for introduction to ceramics ART 2170

Material Amount Batch Subtotal
Frit 3124 30
Gerstley Borate 26
Neph Sye A270 20
Silica 10
EPK 5
Glomax 5
Lithium Carbonate 4
Total Base:100
Mason Stain 6028 Orange 7
Total: 107

Percentage Analysis

Ingredient Amount SiO2 Al2O3 B2O3 MgO CaO Li2O K2O Na2O KNaO P2O5 Fe2O3 TiO2 LOI
Frit 31243016.592.974.134.220.21.892.09
Gerstley Borate263.850.266.970.915.040.11.041.140.030.10.037.67
Neph Sye A2702012.044.720.080.972.083.050.020.1
Silica1010
EPK52.291.870.010.010.020.020.010.040.020.74
Glomax52.662.220.020.020.040.020.050.02
Lithium Carbonate41.632.37
Mason Stain 6028 Orange7
Total10747.4212.0411.10.929.361.631.325.026.340.040.180.0910.9
100% no LOI 53.2213.5112.451.0310.51.831.485.647.110.040.20.1

Unity Molecular Formula (UMF)

FLUXES

RO/R2O

0.24 Na2O
0.04 K2O
0.16 Li2O
0.49 CaO
0.07 MgO
STABILIZERS

R2O3

0.35 Al2O3
0.47 B2O3
GLASS-FORMERS

RO2

2.33 SiO2
SILICA:ALUMINA

SiO2:Al2O3

6.69

FLUX RATIO

R2O:RO

0.44 : 0.56

SiO2:Al2O3 Chart

Closest 100 neighbors in Glaze.

Click and drag to zoom
Stull Chart
SiO2:Al2O3 Ratio
SiO2:Al2O3 Ratio 6.69

Similar RO/R2O Unity Formulas

R2O3 - STABILIZERS RO2 - GLASS FORMERS RO/R2O - FLUXES
Recipe Name ΔTemp Al2O3 B2O3 SiO2 ZrO2 SnO2 TiO2 KNaO K2O Na2O CaO MgO ZnO BaO PbO Li2O SrO
Wood's Transparent Orange -- Cone 04 05-04 0.35 0.47 2.33 0.28 0.04 0.24 0.49 0.07 0.16
Glossy Clear 2, Woody's Base ARAC 04 0.34 0.47 2.32 0.27 0.04 0.23 0.5 0.07 0.16
Woody's Clear Base Glaze 05-04 0.34 0.47 2.32 0.27 0.04 0.23 0.5 0.07 0.16
Wood's Transparent Base Cone 04 glaze 05-04 0.35 0.47 2.33 0.28 0.04 0.24 0.49 0.07 0.16
Wood's Transparent Dark Green -- Cone 04 05-04 0.35 0.47 2.33 0.28 0.04 0.24 0.49 0.07 0.16
Wood's Transparent Dark Blue -- Cone 04 05-04 0.35 0.47 2.33 0.28 0.04 0.24 0.49 0.07 0.16
Wood's Transparent Rose -- Cone 04 05-04 0.35 0.47 2.33 0.28 0.04 0.24 0.49 0.07 0.16
Wood's Transparent Purple -- Cone 04 05-04 0.35 0.47 2.33 0.28 0.04 0.24 0.49 0.07 0.16
Wood's Transparent Yellow -- Cone 04 05-04 0.35 0.47 2.33 0.28 0.04 0.24 0.49 0.07 0.16
Clear Lee's 04 0.35 0.47 2.34 0.27 0.04 0.23 0.5 0.07 0.16
Val Cushing V.C. Three 04 0.3 0.45 2.38 0.29 0.04 0.25 0.52 0.04 0.15

No reviews yet.

Hazards

09/2016 Note: This is a new feature. If a recipe material is not listed, that material's data has not yet been added. Some materials only have GHS ratings, while others only have HMIS ratings. Warnings differ between systems and countries. Glazy does not take any responsibility for accuracy of linked SDS information. Contact your ceramics supplier for safety information for your specific materials.
Globally Harmonized System (GHS) Hazardous Materials Identification System (HMIS) SDS Link
Material Pictograms Signal Word Hazard Statements Health Flammability Hazard Protection
Gerstley Borate
Neph Sye A270
Silica HarmfulHealth Hazard DANGER From 200-Mesh SDS:
May cause cancer by inhalation.
Causes damage to lungs through prolonged or repeated exposure by inhalation.
* 0 0 E
EPK HarmfulHealth Hazard DANGER EPK Kaolin is a naturally occurring mineral, which may contain amounts of crystalline silica
typically 0.1-1.0%, may cause damage to respiratory system through prolonged or repeated
exposure.
1 0 0 E
Lithium Carbonate Harmful WARNING Harmful if swallowed.
Causes serious eye irritation.
Harmful to aquatic life.