Category: Glaze > Clear
Created 2015-08-27 08:10:50 by Glazy Admin
Categories: Glaze > Clear
Firing Temperature: Δ6
Atmospheres: Oxidation
Surface Type: Satin - Matte

Source/Alternate names: Cushing Handbook 1994 Smooth Satin/Mat Base

Firing Notes: cool maximum rate to 800C hold 1 hour

Significant Flaw: crazing

Notes: Alisa Clausen: glossy, transparent base, crazed badly on white midrange stoneware, oxides did not move under glaze.
With 10 zirconia, glossy, white glaze, crazed on white midrange stoneware, oxides did not move under base.
With 2 cobalt carbonate, glossy, dark blue glaze, no visible crazing.
With 1 cobalt carbonate plus 2 chrome oxide, semigloss, dark green glaze, no visible crazing.
With 1 copper carbonate, very glossy, transparent glaze, light green, crazed.
With 10 ochre, slightly less glossy, ochre brown glaze, slight crazing.
With 10 red iron oxide, slightly less glossy, dark brown glaze, no visible crazing.

Notes: Steve Slatin: some of the Cushing glazes are formulated for the far edge of what works. My favourite, Rusty Bronze done as green
runs at cone 6, and if you have a cool at all slow it gets very matte, but if you turn off your kiln at cone 5½ and do a fast cool, you get a
fabulous mix of glossy where thick and microcrystalline with a nice texture shift where thin. And one percent of bentonite in the glaze
bucket just changes it entirely.

Material Amount Batch Subtotal
Nepheline Syenite (Theoretical) 45
EPK 20
Whiting 18
Zinc Oxide 12
Silica 5
Total Base:100
Cobalt Carbonate 1
Total: 101

Percentage Analysis

Ingredient Amount SiO2 Al2O3 MgO CaO ZnO K2O Na2O KNaO P2O5 Fe2O3 TiO2 CoO LOI
Nepheline Syenite (Theoretical)4527.3210.480.050.312.074.416.480.040.32
EPK209.157.470.020.040.070.010.080.050.150.082.96
Whiting1810.17.9
Zinc Oxide1212
Silica55
Cobalt Carbonate10.630.37
Total10141.4617.960.0710.45122.144.426.560.050.20.080.6311.55
100% no LOI 46.3520.070.0711.6813.422.394.957.340.060.220.090.7

Unity Molecular Formula (UMF)

FLUXES

RO/R2O

0.17 Na2O
0.05 K2O
0.34 ZnO
0.43 CaO
STABILIZERS

R2O3

0.41 Al2O3
GLASS-FORMERS

RO2

1.61 SiO2
OTHER

 

0.02 CoO
SILICA:ALUMINA

SiO2:Al2O3

3.92

FLUX RATIO

R2O:RO

0.22 : 0.78

SiO2:Al2O3 Chart

Closest 100 neighbors in Glaze > Clear.

Click and drag to zoom
Stull Chart
SiO2:Al2O3 Ratio
SiO2:Al2O3 Ratio 3.92

Similar RO/R2O Unity Formulas

R2O3 - STABILIZERS RO2 - GLASS FORMERS RO/R2O - FLUXES
Recipe Name ΔTemp Al2O3 B2O3 SiO2 ZrO2 SnO2 TiO2 KNaO K2O Na2O CaO MgO ZnO BaO PbO Li2O SrO
Blue Val Cushing Smooth Satin Matte (+1 Cobalt) 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
Val Cushing Smooth Satin Matte Base 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
Val Cushing Smooth Satin (+ Red Iron Oxide) 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
Dark Blue Val Cushing Smooth Satin Matte (+2 Cobalt) 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
Dark Green Val Cushing Smooth Satin Matte (Cobalt & Chrome) 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
Green Val Cushing Smooth Satin Matte (+Copper) 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
VC Smooth Satin Mat, 1 Cob.carb,2 Chrome ^6 ox. 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
VC Smooth Satin mat, 1 Cu. carb. ^6 ox. 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
VC Smooth Satin Mat, 10 RIO ^6 ox. 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
VC Smooth Satin Mat, 10 RIO ^6 ox. (variation) 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
VC Smooth Satin Mat 1 Co.^6 ox. 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
VC Smooth Satin Mat base ^6 ox. 6 0.41 1.61 0.22 0.05 0.17 0.43 0.34
Satin Matte Light Brown 6 0.43 1.63 0.22 0.05 0.17 0.43 0.35

No reviews yet.

Hazards

09/2016 Note: This is a new feature. If a recipe material is not listed, that material's data has not yet been added. Some materials only have GHS ratings, while others only have HMIS ratings. Warnings differ between systems and countries. Glazy does not take any responsibility for accuracy of linked SDS information. Contact your ceramics supplier for safety information for your specific materials.
Globally Harmonized System (GHS) Hazardous Materials Identification System (HMIS) SDS Link
Material Pictograms Signal Word Hazard Statements Health Flammability Hazard Protection
EPK HarmfulHealth Hazard DANGER EPK Kaolin is a naturally occurring mineral, which may contain amounts of crystalline silica
typically 0.1-1.0%, may cause damage to respiratory system through prolonged or repeated
exposure.
1 0 0 E
Whiting Harmful WARNING Causes eye irritation
Zinc Oxide 0 0 0 *
Silica HarmfulHealth Hazard DANGER From 200-Mesh SDS:
May cause cancer by inhalation.
Causes damage to lungs through prolonged or repeated exposure by inhalation.
* 0 0 E
Cobalt Carbonate Health HazardEnvironmental Hazard DANGER May cause cancer
Suspected of causing genetic effects
May damage fertility or the unborn child
May cause allergy or breathing difficulties if inhaled
May cause a allergic skin reaction
Very toxic to aquatic life
Very toxic to aquatic life with long lasting effects
2 0 0 *