Category: Glaze > Shino
Created 2015-10-19 03:21:34 by Terry Rorison
Categories: Glaze > Shino
Firing Temperature: Δ6
Atmospheres: Oxidation
Surface Type: Satin
Transparency: Opaque
Material Amount Batch Subtotal
Dolomite 23.3
Spodumene (Theoretical) 23.3
Kentucky OM #4 Ball Clay 23.3
Silica 23.3
Frit 3134 6.8
Total Base:100
Tin Oxide 4.85
Yellow Ochre 3.24
Red iron oxide 1.07
Total: 109.16

Percentage Analysis

Ingredient Amount SiO2 Al2O3 B2O3 MgO CaO Li2O K2O Na2O KNaO Fe2O3 TiO2 SnO2 LOI
Dolomite23.35.17.111.09
Spodumene (Theoretical)23.315.056.391.87
Kentucky OM #4 Ball Clay23.312.866.50.090.070.230.070.30.260.282.94
Silica23.323.3
Frit 31346.83.161.571.370.70.7
Tin Oxide4.854.85
Yellow Ochre3.241.870.650.010.71
Red iron oxide1.071.020.05
Total109.1656.2413.531.575.28.551.870.230.7711.980.284.8514.08
100% no LOI 59.1614.231.655.478.991.960.250.811.052.090.295.1

Unity Molecular Formula (UMF)

FLUXES

RO/R2O

0.03 Na2O
0.01 K2O
0.17 Li2O
0.42 CaO
0.36 MgO
STABILIZERS

R2O3

0.37 Al2O3
0.06 B2O3
GLASS-FORMERS

RO2

2.61 SiO2
0.09 SnO2
0.01 TiO2
OTHER

 

0.03 Fe2O3
SILICA:ALUMINA

SiO2:Al2O3

7.05

FLUX RATIO

R2O:RO

0.22 : 0.78

SiO2:Al2O3 Chart

Closest 100 neighbors in Glaze > Shino.

Click and drag to zoom
Stull Chart
SiO2:Al2O3 Ratio
SiO2:Al2O3 Ratio 7.05

Similar Base Recipes

Δ6 - 7

Similar RO/R2O Unity Formulas

R2O3 - STABILIZERS RO2 - GLASS FORMERS RO/R2O - FLUXES
Recipe Name ΔTemp Al2O3 B2O3 SiO2 ZrO2 SnO2 TiO2 KNaO K2O Na2O CaO MgO ZnO BaO PbO Li2O SrO
Nutmeg Shino Cone 6 Sugar Maples 6 0.37 0.06 2.61 0.09 0.01 0.04 0.01 0.03 0.42 0.36 0.17
Nutmeg Shino Cone 6 Sugar Maples (Toms UK GB variation) 6-7 0.37 0.06 2.62 0.1 0.02 0.01 0.01 0.42 0.37 0.18
Nutmeg Richard Busch's 6 0.38 0.06 2.65 0.09 0.01 0.05 0.01 0.04 0.42 0.36 0.17
WWW 486 6-7 0.35 0.06 2.65 0.09 0.01 0.05 0.01 0.04 0.43 0.36 0.17
Chromed Nutmeg 5-6 0.38 0.06 2.65 0.09 0.01 0.05 0.01 0.04 0.42 0.36 0.17

No reviews yet.

Hazards

09/2016 Note: This is a new feature. If a recipe material is not listed, that material's data has not yet been added. Some materials only have GHS ratings, while others only have HMIS ratings. Warnings differ between systems and countries. Glazy does not take any responsibility for accuracy of linked SDS information. Contact your ceramics supplier for safety information for your specific materials.
Globally Harmonized System (GHS) Hazardous Materials Identification System (HMIS) SDS Link
Material Pictograms Signal Word Hazard Statements Health Flammability Hazard Protection
Dolomite Health Hazard DANGER May cause cancer (Inhalation) 1 0 0 E
Spodumene (Theoretical) Health Hazard DANGER May cause cancer by inhalation.
Causes damage to organs through prolonged or repeated exposure.
Kentucky OM #4 Ball Clay Health Hazard WARNING May cause damage to lung through prolonged or repeated inhalation 2 0 0 E
Silica HarmfulHealth Hazard DANGER From 200-Mesh SDS:
May cause cancer by inhalation.
Causes damage to lungs through prolonged or repeated exposure by inhalation.
* 0 0 E
Tin Oxide Harmful WARNING Harmful if swallowed.
Yellow Ochre Health Hazard DANGER May cause cancer.
Red iron oxide Health Hazard WARNING May cause damage to lung through prolonged or repeated exposure by inhalation